Oh, this is lovely info, thank you! I love math, haha. Is it possible to combine hardnesses such that parts of the mold are harder and other parts are softer? (For example, a baby doll with soft cheeks but a firmer skull/soft tummy but firmer ribs/spine) If they’re all platinum cure and layered while curing, will they merge together, for example? Will it be a gradient of hardness levels or an abrupt difference? (Is it possible to achieve both depending on when you introduce the different hardness silicone?) There are all sorts of videos of people making extra-extra soft silicone dolls-do you know if they’re probably adding silicone oil or slacker (or something else?) to achieve that? Hope all the questions are okay. I’m trying to work out which products I would need to purchase for a project I’ve been thinking about.
Hi, I was wondering what your 2kg of silicone cost & the name of the products.? Loved your video I have watched other videos using silicone in the tubes. I want to make larger candle moulds like yours. If you could let me know that would be great. Thank you 😎
The Answer is no, tin cure silicones are not skin safe. Meaning they cannot be used for life casting. Even platinum cure silicone needs to be officially certified as skin safe. If you are life casting, you need to look for skin safe Platinum cure silicones that can be applied to the skin with a paint brush.
I accidentally added significantly less hardener than I should have to my tin cure silicone. I just found this out after having the mold in the pressure pot for hours already. Should I be patient or is the mold lost. I added about 2% (my usual B compound) when it should have been 5% (accidentally used wacker t21)
I have purchased your product and now ready to start making moulds. I am urgently needing a Lotus Biscoff mould. Am I able to use a biscuit to make the mould? Of course, the biscuit will be thrown away thereafter.
@@silicreate I think they're asking why you shot a visual demo of white material against a white background. It would have been a much clearer demonstration against a dark background.