Thank you very much!!!!! I greatly appreciate what you are doing! I watch your lectures and videos and they are a great help to me! Please continue doing the good work! You are inspiring!
@@abaqusacumen7397 Hello sir... I want your support for abaqus simulation for my B.Tech project... can you plz help me... I am ready to pay your charges.
Thanks a lot for uploading the video! As a suggestion for similar videos, you could make a video of an axyssimetric rubber seal being compressed by rigid surfaces. It will not be difficult to do and people will like it
Thanks for the sharing such precious information, Will you please make a video on the material constants for steel subjected to cyclic loading. Material parameters for isotropic hardening and kinematic hardening.
hello Thank you for preparing these valuable videos. I would like to ask you to make a video for abaqus/matlab interface. call the abaqus with matlab. run the abaqus with matlab. and import the result from abaqus to matlab.
Thank you sir for this informative vedio, Can you please upload video for Anisotropic Hyperelastic materials? How can I find the parameters for Holzapfel model, C10, D,k1, k2, and kappa
what determines whether a material is stable or not? (it's shown in your Stability Limit Information window). Is it related to Drucker's stability criteria?
Hi sir, I would like to ask you for some help. I am using hyperfoam to model Polyurethane. I am inserting a compression data set to fit a 2nd order strain energy potential. The model fits the data very well for strains from 0.1 to 0.8. However, my model does not catch the elastic behavior coming from the experimental data. the experimental stress is double that predicted by the model in the strain range from 0-0.1 (the range of cell walls bending). This appears clearly when I run my simulation and also when I evaluate the material. Is there any suggestion to solve this issue? thanks.
Thank you for your lecture, sir! I have a small question relating to the test. Could you please let me know What type of stress & strain is used for the test data? I mean they are mises equivalent stress/strain or stress components? Thank for your help, sir!
Hi, thanks for such a good video. Anyways, I have 2 questions. (1). why the Ogden constants that you generated are different from those provided in the paper? (2). can we use the Ogden constants which we generated in Abaqus for material input in LS-Dyna simulation? I noticed that even we use the same nominal tensile stress strain of the material and generate the material constants, those constant generated from Abaqus are different from those generated from LS-DYNA. Anyone please correct or give me some ideas on this. Thank you in advance.
Here you have used test data .. what if we dont have test data and use hyper elastic material with coefficients only .. how to derive the equation U... What is I1 and I2?