even if I pass material science with good no, I am not going to unsubscribe this channel. the only way I can show respect to these great teachers of IIT is by subscribing the channel.
In point of Discussion about Effect of temperature in creep ...... When ambient temperature is further increase above( 0.55 of melting temp of materials ) creep is more significant .............. & Increased so on... Results to be Material will be failed under creep( like Fusion tungsten bulb) .... In this overview my Question is Can there is not any Effect of thermal stress and strain ...... because we know €(thermal srain) is directed proportional to temparature ?????? Please giving yours valueable feed back sirrr ....🙏🙏 Your faithfully sibam majumdar....
Is it correct sir: Power law creep acts in moderate stress regime.....in high stress regime we find exponential creep law...and in low stress regime we find power law creep with low n...or linear mostly.,.
Sir I have one doubt As we apply load on any material constantly Strain will increase with respect to time right sir But you said that with increase stress creep life will decrease Here my doubt is As we apply stress on constant load strain will increase na sir It mean at first time t=0 no elongation As we go on apply stress strain increase and also time also changed mean timely Then creep life must increase right na sir you are saying it will decrease I can't can you elaborate some more
Creep life is time to failure at a given temperature and stress. If at the same temperature another test is done at a higher applied stress then the material will fail in a shorter time, so will have lesser life.