@@saranyadevi6468 If you can process angle beam flaw detection, thickness/corrosion surveys should not be an issue. If you need to refer to a RU-vid video to find internal pitting with 0 degree, you probably shouldn’t be scanning.
Sir I have a thesis on ultrasonic testing of arc welded mild steel plates. I have got screenshot of the echo but I am unable to identify what type of defect it is can you please help me sir?
If I was scanning with my beam parallel to the weld searching for transverse cracks. How would that typically represent on the A-scan? Similar to the root and toe Crack? Wide base with high amplitude?
Correct, are you scanning on a plate or pipe? On a plate it should be as you have described, on a pipe as well, however because of the curvature of the pipe your root and cap echos will be after half and full skip or at least it will seem that way. In both cases a 45' probe should work best. As always, please revert to your procedure for more detailed input.