Rotten hammer restoration 

Thank you very much for your comment 🙂👋🏻

Thank you.

Thank you.

Thank you.

Thank you PZL for comment. I have wanted to keep all parts original. Now the handle works good. Good luck 👊

Thank you for your comment. I am glad you like it 🙂

Yes, during grinding original marks has disappeared. The hammer is little bit lighter now, but about few grams only.

You do not need accurate amp level for rust removing. Cell phone charger is good for this work because its level of amps is between 1 to 2 A. Does not matter level in this case. But If you would like to make a metal plating (for example nickel plating) you will need correct amp level. And in this case the phone charger is not good. In this case you will need reguratable power supply I have used in this video ru-vid.com/video/%D0%B2%D0%B8%D0%B4%D0%B5%D0%BE-maIdXH0V6Rg.htmlsi=yiVTihj0YPdpUup1 because 1 A is too much for this work.

Thanks I didn't knew that, almost every time I saw someone on yt rust removing by electrolysis they had a power supply. When doing electrolysis this way does the surface of the metal or the quantity of liquid matter? Can you use a phone charger for all your rust removing needs?

​@@Enigmaking I do not want answer wrong. But in my opinion the more metal for anode you use the better and mainly quicker process could be. I use adequate amount of liquid. Not more than necessary and till this time it has always worked :) Thank you for comments and good luck in your project. I hope my answers were useful.

Thank you, your answers are extremely helpful.I have an old rusted axe head that I'm going to restore and I think I will use electrolysis for the first time. Where are you from Mlenski?

@@Enigmaking Czech republic.

My philosophy is to restore as much as possible. Including the rotten handle. Thank you for your comment 👍

Hello, friend. Thank you very much for your useful comment.👍 I really appreciate it. Actually you are not first person who told me. Which means the lengh of some of my videos is serious problem. I just want to show as much steps of process as possible.🙂

I've had to. 😉

Looks correct :)

I have two reasons for derusting. I want to see all damages clearly and I don't want to mess my files with rust. I always want to keep as much as possible from original tool. Handle is fine now. It fits perfect. 😉