Congratulations. Very interesting approach. I'm still thinking about how to set the V-notch location to Charpy test since there are several layers in the HAZ after TBW.
please share reference from where you have taken these parameters, like control of heat input or weld overlap.. Please share reference of Parameters what you used in this video.. for temper bead welding.
please share reference from where you have taken these parameters, like control of heat input or weld overlap.. Please share reference of Parameters what you used in this video.. for temper bead welding.
Dear, your approach is excellent. I have a doubt may be i will not be able to convey properly its about "temper bead effectiveness verification" i.e., comaprison of results with pwht & without pwht 1. Are both the results are of same specimen welded by follwing temper bead welding (befor & after PWHT) ?? 2. Or one sample normal weding ( with & without pwht), and then comparing with the sample using temper bead welding (wih & without pwht)