Which LAYER HEIGHT gives you the STRONGEST 3D prints?

Подписаться 575 тыс.

Просмотров 3,1 млн

50% 1

Does thickness matter? Today we'll find out which layer height you should choose to get the strongest prints! I printed test specimens with layer heights from 0.05mm to 0.40mm and measured their strength.
Check out our CNC Kitchen products at cnckitchen.store/ or at resellers www.cnckitchen.com/reseller and on AMAZON (EU) geni.us/s8rYtQ
You can find all of the results also on my blog: www.cnckitchen.com/blog/the-i...
For further reading:
my3dmatter.com/influence-infi...
drive.google.com/file/d/0Bxo6...
www.researchgate.net/publicat...
manual.slic3r.org/advanced/fl...
en.wikipedia.org/wiki/Size_ef...
🛒 Equipment used in this video (Affiliate Links):
Original Prusa i3 Mk3S: geni.us/CNCKPrusaMk3
Prusament PLA: geni.us/CNCKPrusament
💚 Support me 💚
Patreon: / cnckitchen
Join as a RU-vid member!
Buy an Original Prusa i3 printer: geni.us/CNCKPrusa
PayPal: www.paypal.me/CNCKitchen
Shop at Matterhackers(US): www.matterhackers.com/?aff=7479
Shop at 3DJake(EU): geni.us/zHvnB
JLCPCB 3D Prints starting at only $1: geni.us/JLC3DPrinting
🎙Check out my PODCAST with Tom Sanladerer
/ @themeltzone
⚙ My gear (Affiliate Links):
🎥 CAMERAS & LENSES
Panasonic GH5 - Professional 4k60 camera: geni.us/LMN0CmS
Panasonic GX80/GX85 - Great value system camera: geni.us/M2Sm
10-25mm f1.4 - Awesome Lense: geni.us/ZTBH
30mm f2.8 macro - Great Macro Lense: geni.us/vEwqD
12-35mm f2.6 - Great allround lense: geni.us/S9GOsr
14-140mm f3.5-5.6 - My go-to travel lense: geni.us/fSAyKo
25mm f1.4 - Nice prime for photoraphy: geni.us/mqWM
🎙AUDIO
Rode Video Mic Pro - Shotgun mic: geni.us/6JFRdJ
Rode Film Maker Kit - Wireless mic: geni.us/XMD2N
Rode NT-USB - Studio Mic: geni.us/YVONvy
🔴 LIVE STREAMING
Elgatoo Stream Deck: geni.us/ppIiAL
Elgatoo HDMI USB Capture Card: geni.us/imhD
Logitech C920 - Overhead camera: geni.us/ViVgB
🏆 Do you want to help me cover my running costs? Send me a dollar or two over PayPal, it helps me a lot!
www.paypal.me/CNCKitchen
🌼 Even watching the ads before my videos helps me a lot!
Follow me on Twitter: / cnc_kitchen
DISCLAIMER: NONE of these tests were performed with any officially calibrated test equipment. The values presented in this video are for information/entertainment only and will not be comparable to any official tests!

Наука

Опубликовано:

4 июн 2024

Ссылка:

Скачать:

Готовим ссылку...

Добавить в:

Мой плейлист

Посмотреть позже

Комментарии : 1,7 тыс.

@JasonZnack 5 лет назад

The gaps between the layers of your 0.3 and 0.4 prints would indicate that you're printing too cold or too fast for that nozzle size/layer height combo. You even note the under extrusion in the broken part. For more comparable results I suggest you normalize your print settings to make the volumetric flow rate match. The flow rate difference between 0.05 layer height and 0.4 is substantial. If you're not controlling for this difference, your test procedure will favour the lower layer height parts substantially. I think this warrants future investigation.

@cthulpiss 5 лет назад

Still - these were printed @ 215C, that should be quite enough for PLA + Prusa combo.

@JasonZnack 5 лет назад

@@cthulpiss Note he's also using a hardened steel nozzle. You can lose 10c at the nozzle tip. Usually needs 10-20c above the recommended temp, especially when pushing flow rate to ensure adequate melt. For me, I print production parts with a 0.6 hardened steel nozzle at 0.3 at 70mm/s. That's pushing around 12 cubic mm/s which is the limit for the V6 block. For PLA I'm needing 220-230 and with PETG 250-260. Lower than that and part strength is definitely affected.

@AustinVojta 5 лет назад

Well explained, this was my first thought too. Needs to print slower for the thicker layer heights and make the flow rates the same.

@JasonZnack 5 лет назад

@@AustinVojta Yes and in this case I think flow rate is just a proxy for Time in Melt Chamber. I also noted that he had clogs at the 0.05 layer height. Probably due to the flow rate being too low and the filament cooking in the chamber.

@cthulpiss 5 лет назад

@@JasonZnack Could you please point me to some math data around that V6 block thermal capacity vs. materials like PETG and ABS?

@conorsweeney7483 5 лет назад

7:53 is the actual test

@jaredtmorris 4 года назад

Doing gods work there bud

@compositebow151 4 года назад

Thank you good sir

@leestons 4 года назад

Thank you!

@akorkmaz074 4 года назад

THANKS

@alb.1911 4 года назад

thanks god.

@HunGredy 4 года назад

First I was like what the hell kind of music is this, then I realized it's the sound of the testing machine.

@Oretal 4 года назад

HunGredy Dude I thought the same thing.

@V843v3r 4 года назад

not gonna lie, it kinda sounds good with the music

@hawkbatcustoms3172 4 года назад

Same

@phminiaturas 3 года назад

The test machine makes a sound which is roughly similar to a Moog keyboard in the tone of C sharp. The actual background music, being in the key of F sharp minor, fits in perfect harmony with it.

@jakemancnc 3 года назад

Haha I would of never noticed

@KimJerbo 2 года назад

Why am I watching this at 2am? I don’t have a 3d printer and are not planning to get one…

@CNCKitchen 2 года назад

Hope it still was worth a bit of your time 😅 have a good night.

@joeldriver381 5 лет назад

I mostly make functional parts and love this type of data. Excellent work!

@iteerrex8166 5 лет назад

Exactly Joel! This is awesome!

@williamlewington3223 5 лет назад

Feel like almost everyone in 3D printing is just making pretty models, thank god for this type of video!

@mikehawk4517 5 лет назад

@@williamlewington3223 Agreed. That's what I see so much from 3D-printing too; people making "pretty" models. But I just love it when 3D-printed parts actually are useful and have a functionality. But of course, that's when material strength usually has a more important role and that's where videos like this one are great.

@Ricky_B4 5 лет назад

@@williamlewington3223 No! Thank Stefan for this type of video.

@jefdamen2977 5 лет назад

This why germans make great stuff :) They ask great questions although they might seem picky to others.

@levih.2158 Год назад

8:24 - Horizontal print comparisons (9:05 - conclusion) 10:29 - Vertical print comparisons

@Filiaris1 Год назад

Thank you😊

@ElectroDOG1789 7 месяцев назад

Thanks

@CaptainSkinnySK 4 года назад

CNC Kitchen: *prints super detailed and intricate part My prints: 12:18

@bldjln3158 3 года назад

That’s CNC Kitchen’s print.

@TheSnipers9 2 года назад

@@bldjln3158 :o

@PWNHUB 2 года назад

1:35 This is directly effected by direction of your print. Thinner layer height would be better with the grain, and thicker layer height against the grain.

@TheMarkrafter 5 лет назад

I just ordered my first 3D printer and must say as an engineering student I greatly enjoy your videos! I look forward to seeing more of your videos in the future.

5 лет назад

Thank you for putting all that effort into testing these 3D printing parameters for us. This information is very useful and you have just saved us hours of testing. Danke schön!

@CodeCowboy64 4 года назад

I really appreciate not only your video's subjects, but the quality of the videography and video editing. You make things very clear visually along with your narration. Subscribed! Thank you!

@batlin 4 года назад

This is a good demonstration of why it's important to make sure your layers aren't stacked parallel to the load direction. I didn't realise it was so critical to tensile (and probably compressive) strength.

@TiocfaidhArLa34 9 месяцев назад

its kinda like splitting wood against vs with the grain.

@phenax1144 9 месяцев назад

Idk know about compression i think that it will be stronger in compression’s when stacked parallel

@Kspice9000 6 месяцев назад

@@phenax1144it would definitely be stronger in compression.

@MassholeMachinist 3 месяца назад

@@Kspice9000 I agree but the direction force is giving inaccurate results in this experiment. If he compressed the hook at the same point it would have torn from the outside edge instead of the inside edge from pulling. I bet if the force was applied evenly around the section being tested it would have withstood more.

@connorp6861 5 лет назад

I’m currently working on some heat treatment methods of PLA for strength gardening. It has been done in the past but not clearly defined in any reports. After heating in an oven for an hour at 220°F I recorded my PLA prints to have almost a 30% increase in strength between layer lines. I also tried boiling and quenching my prints with similar (but not as great) results. Might be something interesting for you to try!

@zickentrainer 2 года назад

Yes conditioning should improve the mechanical attributes of any Thermoplast.. The issue is to get the "right" procedure... which means temoerature and time and when to do it... I would say it's to be done imediately after the print at a temperature somewhere between Printing bed temperature and max. Permanent temperature of the material.. (and except PA) it definiteky, should be in a dry environment.. With PA it could be that boiling it, maybe the right procedure.. Everything else I would definiteky go for the oven.

@mickmouse2258 2 года назад

There's a lot of discussions out there that address annealing. Yes, you can get some pretty nice strength increase from a simple "heat and hold then cool" where time and temp are the only considerations, but I learned from doing flame glass work that there's a bit more to the science of annealing. Results widely vary dependent on the material, with some showing great increase and some showing virtually none. Additionally, "stepped" heating and cooling stages can make dramatic differences in the molecular rearrangement. It really depends on if you're just doing a "quickie" for a simple print or trying to make a particular item as strong as it can be. One other BIG factor in some jobs is that reheating and cooling the part can result in SIGNIFICANT changes in size, made worse by the fact that it's usually different in different axes. Z usually shows little change, with X and Y showing amounts that differ from each other AND Z. This is a real nightmare if you're making a interlocking or sliding part that joins another! So yes, for a simple part, many plastics do show some strength increase but it's HIGHLY variable and you may find yourself reprinting from the unintended size changes. Tip - Many of the better filament producers give annealing info on their web pages or will tell you if you ask them. Same for the proper drying time and temp as many plastics are hydroscopic (absorb moisture) especially the nylon and polycarbonate blends. Printing with "damp" plastic REALLY screws strength and surface finish.

@hotelmor4348 Год назад

may be worth looking into constructing a device that can rotate the part while being heated for tempering, so that gravity doesnt warp the final part

@LogicalWaste 5 лет назад

Love your straightforward and informative videos, Stefan.

@ArcKing01 4 года назад

I love that I actually feel like I'm learning something and enjoying it while listening to you talk about this. Definitely subbed just for that and look forward to more. As for the test itself, it's definitely helping me to think about what methods I can use for my first FDM printer to see the different results. This already gave me a good starting point for when I'm ready to print more than the must-prints and general fixes for the printer I'm getting (Ender 3 Pro)> So thanks a ton for making this video.

@YuriySklyar 4 года назад

YOU ARE THE MAN!!! This is some documentation

@mariom9399 5 лет назад

yep that confirms my experiences, the best results I get with 0,5 mm nozzle and 0,15 layer height, at this settings I get the best looking prints and also the strongest ones

@SeishukuS12 5 лет назад

I would be interested in extrusion width tests, I've been doing a lot of spiral printing in PLA and PETG with 1.2mm width with 0.3mm layer height on my Ender 3, really awesome results (great for making quick boxes), feels really strong too.

@rasantamariat 4 года назад

I'm researching with 3D printed metals and your video has just gave me some ideas. Thank you so much. Excellent video. Liked & subscribed.

@ivanjack8341 3 года назад

I'm new to 3d printing, actually waiting my ender 3 pro to arrive in few days. Your videos answered many questions I had. thank you !

@WeaponGuy117 5 лет назад

I really love how meticulous you are with your tests, and the effort you put into designing the tests so as to eliminate any possible bias. If you even want to revisit or explore this further, it would be interesting to see how using a specialized hotend such as an E3D volcano would change the results, considering that they touted their thicker layers as stronger in their promotional material. Personally I thought the 0.2 would be stronger being a 'balance' between thick and thin, but clearly I need to re-evaluate that line of thought.

@bengriffith5963 5 лет назад

Thank you! I’ve done testing on carbon fiber filled nylon, and .1 layer height was definitely stronger in both planes. Dialed in the settings (with a bit of help of the manufacturer) and now produce incredibly strong parts.

@kwagaming7414 Год назад

I’m very interested in this what did you do?

@JoseAguiloworkshops Год назад

.1 layer height and what nozzle size? Cause if you print CF at .1 with a .4 nozzle you're getting the perfect recipe for a clogged nozzle.

@maximthemagnificent 2 года назад

Designing a weld-less 18650 battery build system around a 0.6 mm nozzle and your videos have been extremely valuable for balancing strength vs print speed. Thanks!

@WillBeebe 3 года назад

The detail is amazing, thank you!

@emotopdx 5 лет назад

So thorough, love how in depth you get and scientific! Although, I can't watch these videos in bed, I doze off! Love you! Keep it up!

@QuinnMorley 5 лет назад

This is an incredible video. Great job, Stefan! I use 0.3mm height quite a bit on my Mk3 and I mistakenly thought that would make things stronger. However, I have a Cr10 set up per your TitanAero video, with a volcano, 0.8mm nozzle, 0.4mm layer height and extruding at a 1.2mm width. I feel the strength in that case is insanely strong. There is probably a relationship to the width vs layer height. You could repeat these experiments with those relationships maintained as the layer height goes up. I think there is more to be done along these lines, and I can't wait to see more videos on the topic.

@dbturbonub2536 2 года назад

Every theoretical idea I have ever had when I 1st got into 3D printing, you have actually taken the time to run the tests! Du bist ganz Toll!!! Prost Herr CNC!!!

@tuchobm 3 года назад

Congratulatons!!! You are doing a good job with all your videos about testing 3D printing. Thank you for helping us to do better 3D printing.

@Sandwich4321 5 лет назад

Please do the same tests with other filament like petg and polycarbonate, because if your printing practical parts you probably wont be using pla for them

@pomprocks 4 года назад

PLA is much more resistant to impacts than petg.

@pomprocks 4 года назад

@@dudemann. ru-vid.com/video/%D0%B2%D0%B8%D0%B4%D0%B5%D0%BE-aODcbK5r5wE.html is the best example i can find how petg compares to pla. petg just completely fails on any decent impact. ru-vid.com/video/%D0%B2%D0%B8%D0%B4%D0%B5%D0%BE-m1I5zttnYjY.html also shows this.

@Volpethrope 4 года назад

@@pomprocks I'm not gonna make a carabiner out of a material that will melt if left in the sun for too long ;P

@holyquack3066 4 года назад

Like your pic but mine is better.

@epicstronkman2455 4 года назад

PLA+?

@type568 4 года назад

This is an awesome topic! Interesting how temperature affects the strength gap of vertically and horizontally printed parts. I'm nearly certain a little increase in printing temperature could add a lot of strength to the horizontally printed(the weaker) hooks.

@zickentrainer 2 года назад

Up to a certain point, more temperature will increase layer adhesion, but may cause u other issues.. Polymeres are a bitch.

@Art_Of_Sound 11 месяцев назад

STEFAN: Your videos are the most well presented, to the point and helpful on YT imvho...been printing for quite a while...always on point!

@kj5xq 4 года назад

I am just getting started in 3D printing. I am very impressed with your demo. Very useful info.

@tristandubin3690 2 года назад

It’d be really interesting to see a test with the print lines angled at 45 degrees throughout the object. It’d take some supports to print, but might combine the benefits of both directions of printing.

@Kotaztrafee Год назад

Interesting. I was think of this. So it's possible?! Oh, you mean tilting the model.?

@DaStuntChannel Год назад

That would make it worse for both lol

@kevinwithrow 7 месяцев назад

Did a owl like that ugly as hell of a print but the ear didn't chip off like on the 90°vertical but that's was cleaner than the 45°

@wo-olf 6 месяцев назад

@@DaStuntChannelnot worse. Instead of 100% vertical but zero horizontal strength it would be 50%/50% which, depending on the circumstances is actually the better deal.

@DaStuntChannel 6 месяцев назад

@@wo-olf a bit more isotropic

@franzolielectronics 3 года назад

Great work!

@dhonnano7417 3 года назад

@rubenithyt 3 года назад

@phenixtechyt 3 года назад

@SkidFace 3 года назад

Dude! Amazing seeing you here! I know you prob get this a lot, but I love what you do with tesla coils!

@weirdness3065 3 года назад

Hi 🐑

@paulopmaker8757 4 года назад

Thanks for this channel. It saves my time and effords. Greetings from Ecuador, Stephan.

@TheStangSlayer 2 года назад

Great analytical look into this. Great work Stefan!

@TredecimMusic 2 года назад

7:00 I’m intending to 3D print minis, so this particular part was nice!

@p_mouse8676 5 лет назад

Great test as usual! Since you always test 3 parts, the only thing I am really missing is some error bars with a standard deviation (2 sigma (σ) would be fine here I guess) in the first test.

@PrintThatThing 4 года назад

Great video! Thanks for the tips :) This was very helpful and I loved seeing all the data.

@LemonInTheSky 4 года назад

Excellent job! Thank you for sharing this!

@3dtwerking324 4 года назад

I think another good test is strength vs print speed. Temperature would also play a role I would thing. I would assume there is an optimum speed for layer adhesion with lower speeds allowing the nozzle temp to somewhat transfer through the hot extrusion heating the previous layer.

@Magic-Smoke 5 лет назад

I'm wondering if these results would change significantly (in terms of the strongest layer thickness) if the parts were annealed?

@johnsantiago7836 3 года назад

I have been wondering about exactly these questions - many thanks for your effort. Thanks also to those offering testing protocol insight (e.g. J Z); the conversation helps us all understand the variables to continue experimenting.

@movax20h 4 года назад

Great video. So much work and useful information! I home you continue testing physical properties of 3D printed parts. It is really cool research topic.

@thedadgeek4793 3 года назад

Donate to this man. He is doing a great service. Thank you Stefan!!! You rock.

@10p6 4 года назад

My favorite settings are using 0.3 mm adaptive layers in Cura. Prints quick, looks pretty good and seems more than strong enough.

@Kirillissimus 2 года назад

I prefer 0.2..0.25mm as it gives the nicest looking prints but 0.3 is still somewhat decent as well. 0.1 and below gives nasty and unstable results on my printer and with 0.4 the layers do not stick wery well especially with cheap plastics from China and the process tends to give very fragile parts and with thin walls it can easilly not even get printed successfully at all. I would say that 0.2 is the sweet spot, 0.15 is for small parts with small features and 0.25 is for when you are in a hurry.

@ATLRIOT 4 года назад

This was really well done. Thanks for taking the time.

@funguy4900 3 года назад

Great video. You’re the best at performing testing with valid results.

@elvinhaak 5 лет назад

Please test with different nozzle-sizes and combined with the layer-hights.

@InformatrIIcks 5 лет назад

Wow ... Wasn't expecting that at all ... I even bought a 0.8mm nozzle "to make stronger part" back in the day, because i was thinking that 0.6mm layer height would improve the strenght of my parts ... Thanks for your work !

@piccoleitor 5 лет назад

But maybe layer width can improve strength

@sepid129 5 лет назад

You are misunderstanding this test greatly. The point is for same nozzle size what layer height is going to be the strongest. Bigger nozzle will give stronger prints.

@Dave_the_Dave 5 лет назад

You also need a hotend that can supply enough heat to the much higher amount of plastic flowing through it. The ability to get heat into the plastic is going to determine your max print speed.

@KevinErhardt 3 года назад

I very like your in-depth and systematic tests! Well done! Some weeks ago I ordered a Prusa Mini and currently waiting for it's delivery. In the meantime I'm getting through the theory of 3d printing and got hooked by your channel. One of the questions I have is about the 3d model orientation on the heat bed, especially the quality of the strength of final print. Would be great do get an insight into the way you do your tests! Best wishes from Münster, Germany

@thegeneralissimo470 2 года назад

I love how the separation looks so clean when they snap.

@jonhon 5 лет назад

0.16 layer height is what I always use for perfect models, 0.2 if it doesn't have to be perfect, and 0.32 for prototyping. On a .4 nozzle.

@icenic_wolf 3 года назад

Have you ever tested the strength of hooks printed at 45 degrees from vertical to compare with the horizontal and vertical ones? I'm wondering if there's any benefit, and if so, is it worth the extra filament used for the supports that I'd assume you'll have to use?

@nathanbasset 4 года назад

Incredibly well put together!

@Lilithe 4 года назад

Wow, what a lot of work! Thanks for doing all this. I usually print at 0.2 but I might try 0.15 for things that require strength.

@strictnonconformist7369 3 года назад

I’d be curious to see a comparison of infill patterns along with their wall thicknesses, as well as the amount of overhang the higher layers have over lower layers: unless you’re making a vase where there’s not much change in that regard, I strongly suspect that makes a larger impact than you’d think. As an example of infill geometry differences, consider a strictly honeycomb grid with all vertical walls for a given infill percentage compared to also doing a honeycomb grid of prisms growing/shrinking: intuition suggests the vertical walled honeycomb grid would be stronger for layer adhesion between layers, but there are also intuitive thoughts to consider perhaps a non-regular vertical pattern may also be stronger by mixing up what’s stretched and where, for leverage.

@troybaxter Год назад

That would be a good idea. Plus, given that we know the properties of 0.05 to 0.2 are roughly the same, we can just print at one of those settings.

@grindsman22 5 лет назад

I'd like to know how to get the strongest possible layer adhesion with high temperature filaments like nylon or polycarbonate

@ILovePancakes24 3 года назад

Buy, and test, and find out

@koosik6651 3 года назад

I love those scientific graphs. All this research is quite professional so it's really useful. Great job!!

@rb-ro2po 2 года назад

Thanks for doing these tests and your knowledge

@samaipata4756 3 года назад

Hallo Stefan, I think what you proofed beyond any doubts is the fact how many fold, complex and different the factors are, impacting those test results. One thing I noticed that got forgotten is humidity. I could imagine that there also might be a sweet spot to be found in which a certain filament will develop its maximum strength. I think you do an exceptional good job at creating awareness about the challenges of fine tuning a 3d print. As I’m still new to 3d printing with little to no experience your tests sure are an eye opener about the true science behind this technology. And it is very interesting to read all the comments of obviously highly knowledgeable follower of yours. Thank you and to all who contribute to this excellent knowledge exchange!

@bobbyk452 2 года назад

Hey Stefan, great video! Have you ever tested the effects of not only speed but acceleration on prints? I feel like it's a setting a lot of makers either forget about or don't know about.

@eruma 4 года назад

What a lovely approach to explain the theory behind 3D printing!

@the_junkyard 5 месяцев назад

Thanks for the very educational study. Definitely confirmed print direction plays a huge role in strength

@HobbyHoarder 5 лет назад

This is one of your best videos so far! And yay, new intro. So 0.15mm seems to be the optimal height for both looks and strength. I really love this test. Most people on forums are recommending higher heights for stronger prints, yet that's clearly not true.

@AverageJoe8686 5 лет назад

At the end of the video he says the ~2.6 Nozzle to Layer Ratio might be a better target to meet than just layer height.

@sepid129 5 лет назад

Bigger layer heights coupled with bigger nozzle will be stronger. Here he is looking into nozzle and layer height ratio. I don't see people claiming bigger layer height is stronger, only that bigger nozzle will yield stronger prints.

@stratos9222 5 лет назад

Hobby Hoarder the prettiest parts will be strongest, I suppose!

@HobbyHoarder 5 лет назад

@Blondie SL You should always use 0.2 for the first layer height, regardless of what you use for the rest of your print. It depends for the temp, but for PLA, I usually have 215'C for first and then 210'C for the rest. You can print a temperature tower to test your specific filament. Make sure your bed is really level and do a PID tuning as well.

@evinyatar25 5 лет назад

Can you test the effect of rounding the layer heights to the nearest full step of the z axis motor? I think for the i3 that’s every 0.04mm. CHEP made a video about this some time ago.

@antexa5 2 года назад

I never comment on videos, but actually you are doing an extremely well designed work, scientific with a lot of effort! Thank you!

@andrewut7ya511 Год назад

Sincere Thank you for making this. Im using your data to improve my work. i cant afford school, this is just as good for what i need. Thank you.

@peepzorz 5 лет назад

Would love to see this tested with PETG filament. In my experience PETG has perfect interlayer adhesion and never splits along a layer boundary when testing to failure.

@ferhatkaratasfk 2 года назад

This is called cohesive failure in PETG, which is preferred over adhesion failure in PLA as shown in the video. I expect the cohesion failure mode is better predictable because failure is less dependent of the environment conditions (filament surface impurities) and hence data is expected to show less scatter.

@XRelabs 5 лет назад

man .... I like your work ....keep it up... I have a comment on printing all at once as I am doing my thesis in the strength of the 3D printed part by changing material mainly. I noticed that doing print all at once is weaker and more brittle than printing one at a time parts... in PETG it also changed its behavior from ductile and stretchable to more stiff and brittle but almost same strength. I think you should do a video about that. I can share my results with you if you are interested .... best of luck fellow engineer

@iviaverick52 4 года назад

Great work. tons of time put in that we all appreciate!

@kelpekis 2 года назад

Awsome work man!

@ABaumstumpf 5 лет назад

It would also be interesting how much aceton-smoothing and similar affect the layer-adhesion of different layer heights.

@vincenttremblay-dionne8343 4 года назад

Really interesting videos! I am actually watching all of them. It could be nice to have an all-in-one video combining the optimal parameters to improve, speed, resistance, quality, etc. for most of cases (in other words, resume of all your interesting videos).

@Ibian666 2 года назад

Thanks for doing this. Learning is happening.

@CNCKitchen 5 лет назад

Feel free to share and discuss the video on you Social Media plattform of choice! *NOTE*: Maybe it wasn't 100% clear but I was printing with an 0.4mm nozzle during the tests.

@patriksjoberg9830 5 лет назад

Hate to tell you but the comparison is not proportional as surface contact is increased as the layer height is getting higher as long as you dont compensate with reducing the infill or wall thickness.(and therefore not reflecting the actual strength of the layer size) maybe a topic for a new video?

@billymonday8388 5 лет назад

Whoever wants to know more about this might as well search about stress concentration

@hyperhektor7733 5 лет назад

i would be interested to see 1mm nozzle at 0,4mm layerheight as comparison

@DerSolinski 5 лет назад

Muhaha nailed it, because 1.5 is ruffly 4x nozzle size. I didn't know about the test you mentioned but I always print around 3-4x nozzle size for any mechanical part. (Actually I always try to use multiples of the nozzel size and approx that with a multiple of 1 full step z-distance

@ExEBoss 5 лет назад

Just what in the world of 3D printing happened to result in the situation at 12:30?

@gregorboxer2463 3 года назад

Das „Guten Tag“ hats gerissen. Abo ist da

@sigibaes 2 года назад

The chosen music and your test machine where playing in perfect harmony!

@yourzombiemop8259 3 года назад

0.15 seems to be the sweet spot for strength and appearance on your printer with that filament. Cool!!

@DesignPrototypeTest 5 лет назад

The conclusions of this video are only relevant to a .4mm nozzle. That is very important to note. You touched on the proportionality issue when you referenced the paper at 11:21. This same issue is relevant throughout the entire video. A more accurate scientific study would have changed the nozzle with each change in layer thickness to maintain the proportionality.

@workinghard111 5 лет назад

Correct. This is most likely also a reason where the under extrusion is coming from @0.3/0.4 layer height

@theodorevanrooy6413 5 лет назад

Design Prototype Test you mean more general (not accurate) i think. I pretty much only print with .4 mm nozzle...swapping them out is significant work and I’m guessing most people do the same so it’s valuable for me.

@moczikgabor 5 лет назад

This is a proper study to show that a given nozzle can print at a given layer height range only. It IS shown and summarized in the video, that the optimal layer thickness is proportional to nozzle diameter. Probably it is more important to know what layer thickness to choose for the nozzle you are using, as it is a more realistic scenario that you have a fixed nozzle and you adjust the print parameters than changing the nozzle every time. It would be interesting to see which absolute layer thickness is stronger if all would be printed using it's optimal nozzle diameter, but the test in the video is more of a real world use case.

@bobstro 5 лет назад

I'd like to see the challenge be changed to "print this part as strong as possible" and let experienced makers use whatever techniques they have in their toolboxes and apply them. Even specify a wall thickness and let us tune for that. I'm really bothered by the implication that "0.15mm is best" without more detail. Let me use a different nozzle and extrusion width and see how strong the part can be. Great testing, but incomplete and vague conclusions.

@bobstro 5 лет назад

@@theodorevanrooy6413 If that's the case, then he should have acknowledged up front that 0.30mm layers are at the upper end of what you can print for good adhesion at that nozzle size and 0.40mm is almost guaranteed to produce poor results. The testing is excellent (as always) but the conclusions were vague. A test for "how strong can you print this part with a 0.40mm nozzle" might yield altogether different conclusions if different approaches are used.

@hekkn 3 года назад

How to complete any 3d print in just a few seconds: •1. Get 3d Model •2. Import it into software •3. Set layer thickness to the model's height •4. Print 1 layer

@Slurgical_3D_Terrain_Channel 2 месяца назад

Fascinating. Thank you for doing that. It is helpful

@dougsteel7414 2 года назад

Very useful, thank you for doing this!

@PKTEK 5 лет назад

Im editing a video about foam filling 3D prints. The experiment was *mostly* a successful and I would love to hear about how to strengthen prints. EDIT: The results of my video were pretty amazing! Hopefully you can check it out and see what you think.

@UNSCPILOT 5 лет назад

Printing hollow and filling with resin would probably be pretty stong with the right stuff

@PKTEK 5 лет назад

@@UNSCPILOT agreed, however thick resin can still be incredibly heavy from what I have tested. I just finished my mission, the video is up!

@laharl2k 5 лет назад

Depending on the load packing it full of sand would help. Sand if contained can help with compressiong strength. Unless you use something that sticks to the pla, the main stress will still all fall onto the shells, resin works because it grabs to more pla but foam would have no effect in tensile stress. You should try epoxy mixed with sand, thats one hard cement, your parts will end rock solid

@lastplace199 4 года назад

@@laharl2k his channel looks like mostly props so i don't think putting cement inside his prints would be the best direction.

@cthulpiss 5 лет назад

Considering the microstepping on Z-axis, it seems that 0.12 or 0.16mm layers are best - good balance between printing time and strength.

@RentableSocks 5 лет назад

Not that you're necessarily advocating them, but I have a problem with the "magic numbers" that people like to use. "magic numbers" for layer height are a myth. If microstepping is enabled at all, there's no guarantee that you're starting at a full step at the first layer, therefore you may end up using only microstep intervals all the way up if you set a "magic number" as your layer height. If you want to really use the magic numbers, you should DISABLE microstepping, or cut it down to at least 1/4. This will mean you have better holding torque (better accuracy) for every layer, which is the whole point of the "magic numbers"

@cthulpiss 5 лет назад

@@RentableSocks oh, but I use use exactly 1/4 microstepping. And I make sure to start first layer at full step. And calculating those "magical" numbers seems to be less intense for microcontroller. So.... maybe not so magical after all?

@RentableSocks 5 лет назад

@@cthulpiss how do you make sure you start first layer at a full step? 1/4 microstepping is plenty for Z. you get like 8x the holding torque compared to 1/16 microstepping. just using fewer microsteps in general is less intense for the microcontroller. People using "magic numbers" when they're still using 1/16 microsteps makes me facepalm.

@cmmp5510 2 года назад

Very very good. The unefull thing that I don't like is that I wanted to do the same, but you did it first, while I slept. Wonderful work.

@oakridgereview1359 3 года назад

I absolutely love these videos!! Your data break down is exactly what I need .. absolutely no reason, I just need it 😂

@cosmickatamari 5 лет назад

12:17 abandon ship!!

@Pigeon_FX 5 лет назад

Excellent video.......and the exact inverse of what I would have guessed! (Nice to also know why I was wrong!)

@K3ithM0on 4 месяца назад

Amazing work thanks !

@johnstratairious7936 4 года назад

thank you I have been printing at 0.2 height. very helpful...thank you for taking your time making this video. bless you.

@andrewdalton6973 5 лет назад

"That's what she said"

@Chris--kc9xc 3 года назад

We meet again

@VEC7ORlt 5 лет назад

I wonder if results will be the same for 0.8 or biggers nozzles?

@JamesMartland65 2 года назад

Great job. Raises more questions for the future. Subbed.

@haenselundgretel654 4 года назад

Great video. Very scientifically discussed! Perfect. Thank you very much for the data!

@l3d-3dmaker58 5 лет назад

I knew it!!! I have found out myself that in thicker layers lines don't bond as good, and smaller layers fuse together better, not only in XY but in Z as it heats up the previous layer producing a better bond this is why I always print at .12 if I can, thick layers are bad for strength, I was right! thank you Stefan for this video, it's very informative!!! there are a TON of misconceptions and myths taken as truth in 3d printing, your testing is a godsend, keep doing what you do and let's hope to get rid of misconceptions!!!

@3DThird 5 лет назад

That is not always the case though. I noticed that when printing using my Volcano hotend and setting it to the same temp as my e3d v6 that the filament bubbles because it's too hot. Lowering the temp and printing thicker layers on the Volcano yields much stronger prints than when using a regular e3d hotend. I'd love to see Stefan scientifically comparing them and how they affect strength.

@davidprock904 2 года назад

What if you put your entire printer in a vacuum chamber, and build something under a very strong vacuum!

@enzopontone2227 4 года назад

GREAT work and I appreciate the scientific approach you take! Did you ever try a similar comparison with all parameters fixed and trying different fills pattern?

@pepe6666 4 года назад

i learned a lot from this video. i totally had it backwards initially just like you did. excellent work

@anderswegge6828 5 лет назад

I voted for 0.2mm height as the strongest. My reasoning is that of your tested heights, that is the one that provide the thickest strand without making the layer delaminate in the horisontal plane. I look forward to see the results when I unpause.