Cupellation - from cupel to SILVER bead 

Its very difficult but it does work, and you don't have to heat it to 6000F

Thank you Anis

Wonder if you added an oxygen tank and a big rosebud and cranked the temp if you could speed the process?

Yes, I'm processing 1.8kg at the moment

@@OwlTech333 Thank you for the swift answer!

Glad you enjoyed it

no limit, to the amount of lead you can add, but there is limit to the amount of base metals( especially copper) it can remove from the silver

@@OwlTech333 i see, makes sense Thanks a lot for answering!

no, you can't separate gold from silver or silver from platinum or palladium using cupellation, what you can do is separation of noble from base metals

this is silver

Thank you! 😊

nope actually you need get it pass that flash to get it pure

@@OwlTech333 takk

Yes

So I’ll end up with pure gold and silver when finished with the process with anything less than pure gold

Где-то 10-15 минут

юрий у 900-1200

Спасибо

platinum yes, not sure about rhodium

Usually contacts from relays, contactors, etc are Ag+Pd for hardness 1-5% Pd which tend to stay in Ag as is also noble but increase melting point of Ag...

Yes

олово наверно или слишком много меди

Portland cement

OwlTech thank you sir

@@OwlTech333 Hi! I was surfing for bone ashes cupel and end-up on your video. Is there a diference? TY

@@mysticworld1129 yes, Portland cement is much easier to come by, plus using it dry gives you a cupel in 30sec as shown in the video

i don't think its worth the effort

Will do thanks 😊 I don’t know if you would know anything about this but I heard , I think it was in a reply on RU-vid. Anyway I read that the tungsten carbide contacts could be sold for reuse but I don’t recall the reply saying who would by them, I have a few pounds of them. That was a great video. Before I saw it I thought the only way I could purify silver was chemically “nitric acid”

www.uktoolcentre.co.uk/2530701-pro-torch-propane-set.html

Yes. cupellation is the first form of refining used by the ancients

OwlTech okey. Thanks. I’m new to all this but i get lots of information from your videos! // Michael sweden

wish you all the best my friend!

Sampath Guruge Thank you!

Yes, not a negligible threat: multimedia.3m.com/mws/media/114574O/lead-technical-bulletin.pdf

more like 99.9% I've had silver after cupellation wich was tested with XRF: ru-vid.com/video/%D0%B2%D0%B8%D0%B4%D0%B5%D0%BE-NpQT-5rH59k.html

Now you know :)

do you get any PM drop down in the cement or is it the same as bone ash

@@julianbye5316 same as bone ash

i don't, the cupels are collected for lead recovery

@@OwlTech333 ooh ok, do you have an idea of how the lead is recovered?

@@OwlTech333 Awesome, subscribed. Do you have a video on the lead recovery from the cupels?

@@backwoodsengineer no but i have to make one

I don't think so

xi măng thường

AND = B sure but PLENTY sure *there's LOT OF wind while u make that* meaning = LONG *LIFE* 4 u collegue !!!

P.D: annnnddd ( too ) = NICE video :)

ANNND ( too ) c ya IN THE OTHER life....

Why you put soap on your hands when washing them? Water washes away the soap together with the oils it’s has dissolved. Think of the lead (lead oxide to be precise) as soap

@@OwlTech333 Thank you!

Glad it did

1300c

You can

не хватит

попробуй еще у жены обычный стырить

Jorge Nevarez cement

Dang man I have a 55 gal drum that is this material i am sure ....i have found big lead prills in the drum along with the crushed up material that turns to lead when i hit it with a tourch i can see the gild in it as i pull the flame away...

@@OwlTech333 Compressed bone ash is the standard cupel material. I wouldn't expect Portland cement to be very porous.

@@buggsy5 yet it is, there are three main materials cupels are made from: bone ash, magnesia and cement

ru-vid.com/video/%D0%B2%D0%B8%D0%B4%D0%B5%D0%BE-FW-D3Zu6TJw.html

​@@OwlTech333 Thanks so much for the link. Is it possible to use Cupellation for all silver alloys that are used to make contactor contacts? Although, if tin, cadmium, nickel, etc .... is contained? Thank you very much, have a nice Christmas and keep up the great work.

يسرني

about an hour

обычный цемент

Да понять та можно😀вот в этом процесе смысла нет совсем.Как тигелёк использовать для выпариванья сплава после купиляции свинцом это да,вариант...что бы тигельки не покупать,хотя они дешовые.Это когда с рудами,шлихами мутят и свинец как купелятор и растворитель золота,серебро до 20% поглощает,не катит кароче если когда с щолочами и до 700 градусов.😀Я автора очень уважаю,люблю смотреть,но в этом смысла не вижу.Медь,никель,хром и прочее что есть лигирующие в сплаве будет и никак не очистит этот метод,хоть кислородом продувай сам сплав часами,медь останится.Да и чистить эти сплавы свинцовые жопа,долго и нудно,всё в солях его или упаривать до апупения как автор показал.

Alex 1975 "Медь,никель,хром и прочее что есть лигирующие в сплаве будет и никак не очистит этот метод,хоть кислородом продувай сам сплав часами,медь останится." Извините но ето просто не так (в етом ролике покозал) мед очистилась все полностю. @8:05 металл замерз из-за меди @8:24 Я добавил больше свинца, и процесс продолжался до тех пор, пока серебро не было полностью очищено. Просто когда медь там есть нужно добавлят на 20 раза болше свинца. (1гр. Cu /20 гр. Pb) На конце купеляции остаются только ДМ

@@OwlTech333 с чего он медь вытолкнит от туда?Другие окислятся на воздухе и то не факт при такой плавке.Да это древний как мир способ😀м музеях манеты и изделия,сплавы хрен знает что.Да я этим мутю плавлю 3 года балуюсь,если спициальные флюсы сыпать при купиляции золота может как то почистится от примесей...те что силитра или другое убирёт.Свинец и серебро почистить не думаю😀золото,медь,железо,спутники свинца и прочие всё в серебре с таким методом,полно проб читал из наших мест...от добычи руд.Лаврио,Халькидики..на 1 кг серика до 2 гр рыжика и прочено куча

Можно сам попробувать: Сплавите вместе 1гр Ag ; 1гр. Cu ;22гр. Pb, потом сделайте как показал на ролике. На конце будет только шарик Ag, его вес 1гр.

Где-то 40-50 минут, расход газа незначительны

Спасибо

Not if done right. I can prove it to you by fusing 1g Ag 99.99 % with 5g Pb and the resulting bead will be 1g Ag +/- 0.1%

kind of

Love the music, miss it at times

@@readoryx373 the first one who says he likes it 😄

И в место цемента - магнезит можно попробовать Вроде капели из него делают

на етого шарика не делал но на другие делал ru-vid.com/video/%D0%B2%D0%B8%D0%B4%D0%B5%D0%BE-NpQT-5rH59k.html

помойму там там только свинец и видно!!!!

Thank you!

You don't get a lot of fumes. The lead forms lead oxide which slides down the bead and is absorbed by the cupel. With nitric acid, you generate a lot of nitric oxide fumes - also very toxic.

Yeah just noticed :)

цемент разбивают на порошок, смешивают с мукой и сжигают

И что в результате ?? выделяется металический свинец ??

юрий у точно

800?

Noted!

Jessica Roper the idea of the video is to show the full cupellation process from start to finish, not how I recovered 3g of silver. The purity of the refined silver after cupellation is what matters