Он трубу даже не прогрел,насрал сверху шов и все.провара нет.че за учителя ?ты ещё ток на 15 поставь,чтоб прилипало и говори а чё так плохо дуга загорается
@@gilmarlandim9267an amateur can tell you that weld is garbage strictly because of his tacking the joint closed first. Trapped slag and shit all inside the weld and base metal. Whatever happens after that is still garbage because he didnt fix the first mistake he made, just covered it up
Step 1: Run 16 tacs (don’t clear slag on any of em, why would you?) Step 2: Examine your porosity Step 3: Run a random bead over the top of prior faulty tac mess, 0 tie in with either pieces of metal you’re trying to fuse together Step 4: Get fired
@@Jking0005 Excellent answer. He needs to clean the joint and then get into the habit of running a series of consecutive cursive "e's" to tie both sides in with his puddle flow. The dude is dragging straight down the middle of the long line of tacks, not touching the metal on either side!!! & then videoing it showing it as TRUTH! Ugg!
А Вы хитрец как Я погляжу, когда Вы уложили второй слой, при очистке шва от шлака, мелькнул огромный свищь! Правда Вы так быстро оборвали ролик, что его можно заметить, только при замедленном просмотре!!! У нас у русских есть пословица: "Не можешь срать, не мучай жопу! "
@@user-ev6on4sj4p Причём тут время суток, Вы бы ещё обратили внимание на время года!?!? У Вас ампераж слишком высокий, попробуйте УОНИ-13/55 от "ESAB", держите заготовку под небольшим углом!!
Вы хоть сообщайте субтитрами какой металл толщиной варишь и какой диаметр электрода и название его. А то мелькнул электрод и догадайся сам. И толщина металла ещё догадайся. Одни загадки...🙄 На видео металл наверно толщиной 1,5мм, а электрод наверно ⌀2,6мм и марка электрода 6013.🤔
I bet those stitch tacks didn't penetrate enough and i guarantee that second pass did no good whatsoever. Its not supposed to work like caulking a joint. Its welding... actually joining peices together by melting them evenly as deep as possible so that it's as close to one peice as possible. Not just some crap stuck mostly on the top...even if it looks '"good" to you... it's not.
True, but you wouldn't be getting better monetizing results. People always get comments when something is bad, but nearly as many comments when something is good. This is how you play the game. It's not about the quality of the weld, it's about getting people to interact.
Please post a vid of your magnificent welding skills. We would all be thoroughly delighted to witness a true master welder at work. You armchair experts can do it all!
@@andrewgjenningswhat are you on about? You just said exactly what this guy has done. Its bad welding, so hes called it out. If it was good welding you would see praise
There's some sort of epidemic, tackers everywhere. Just spark and keep that arc running. If the material is too thin weld in direct polarity. Never pause, direct your rod (heat) to the thickest or longer material and just let the puddle do the rest to catch the other part so you don't end up putting a hole in it.
@@user-fx5wr1wr7c Reverse polarity: clamp (Negative), rod (Positive) electrons flow from the part to the rod (Rod heats up 70%, the part 30%). Direct polarity: clamp (Positive), rod (Negative). Electrons flow from the rod to the part (Rod heats up 30%, part 70%). Using direct polarity you can weld thin materials easier because the rod doesn't heat so much and you don't end up melting your part.
Because it is the wrong way, and that makes everyone comment, and artificially creates attraction to the video. It's a way to get more interaction, which affects monetizing.
@@andrewgjenningsniiice, i gotta remember this trick so that I can forget it because there’s nothing spectacular I can do for the world to like what Im doing…so thanks…thanks for Nuffin maaan 🤨
@@edwardneuman6061first pass is supoosed to be a bit colder to avoid burning through. Second pass is supposed to be nice and hot to burn out any remaining impurities, hence the name “hot pass”
Здравствуйте! Я начинающий самоучка. Хочу поинтересоваться у Вас, существуют ли какие,либо средства для облегчения розжига электродов УОНИ? А то на моем аппарате горячего старта нету, а токопроводящая подмазка на торце электрода, которая должна помочь зажечь электрод, не справляется с задачей. Пшикнет раз и всё. И нет её. А дуга так и не успела загореться. Пока обхожусь металлическим порошком из-под заточного станка. Сыплю щепотку в начало стыка и сую электрод в неё. В большинстве случаев, дуга нормально загорается. Но такую подсыпку не везде можно применить.
Dude just no... Your final "pass" did nothing and finishing my inspection class I can tell at least 3 surface faults with the bad camera and quick cut off end, and I don't even want to see what lack of fusion you have. Dude stop welding you are teaching people very bad habits and it just doesn't look that good